RG 1102 XL is a versatile polypropylene homopolymer designed for both extrusion and injection molding applications. This polymer is well-suited for producing raffia, tapes, monofilaments, and dairy product packaging, providing a balance of mechanical properties and processability.
 
Product Description
Type: Polypropylene Homopolymer
Grade Name: RG 1102 XL
Packaging: Delivered in PP bags of 25 kg each, with 50 bags on a pallet, shrink-wrapped by PE to ensure stability and protection during transport.
 
Key Applications
Extrusion and Injection Molding: Ideal for a wide range of applications, including manufacturing raffia, tapes, and monofilaments which are used in various industrial and consumer products.
Dairy Products Packaging: Specifically tailored for packaging applications that require food safety and durability.
 
Product Features
General Extrusion Additivation: Enhanced with additives that improve its extrusion capabilities, making it easier to process and more efficient in production settings.
 
Technical Specifications
Melt Flow Rate (MFR): 5.5 g/10min at 230°C with a 2.16 kg load (ASTM D1238/L), indicating good processability for extrusion and molding.
Tensile Modulus of Elasticity: 1500 MPa (ASTM D638), providing stiffness necessary for high-performance applications.
Tensile Strength at Yield: 34 MPa (ASTM D638), reflecting its ability to withstand significant stress before deforming.
Elongation at Yield: 9% (ASTM D638), measuring its flexibility under tensile stress.
Notched Charpy Impact Strength:
3.5 KJ/m² at 23°C (ISO 179/1eA)
1.5 KJ/m² at -30°C (ISO 179/1eA), showcasing its toughness at varying temperatures.
Vicat Softening Point: 154°C (ASTM D1525), the temperature at which the polymer begins to soften.
Ball Indentation Hardness: 74 MPa (ISO 2039-1), indicating the surface hardness of the polymer.
Heat Deflection Temperature (HDT): 85°C at 0.46 N/mm² (ASTM D648), important for applications involving heat exposure.
Melting Point: 163°C (ASTM D3417), determining the temperature at which the material transitions from a solid to a liquid.
Density: 0.91 g/cm³ (ASTM D792), affecting the weight and structural properties of the final product.
 
Conclusion
RG 1102 XL polypropylene homopolymer is engineered for high-performance in a variety of manufacturing contexts, particularly in extrusion and injection molding. Its robust mechanical properties, combined with excellent processability, make it a preferred choice for manufacturers seeking efficient, reliable materials for applications ranging from industrial tapes to food packaging. Whether used in complex industrial applications or everyday consumer products, RG 1102 XL offers a reliable foundation for durable, high-quality products.